PFM:Ni-Cr-Mo
higher chromium (15%) for improved
oxygen scavenger, reaching out and
essentially gas free alloy with
corrosion resistance. Continum C's
chemically bonding with the feldspar
unparalleled homogeneity and
corrosion resistance exceeds the
(SiO2) and kaolin (K2O), found in all
precise alloy chemistry.
requirements of ISO 22674.
dental porcelains; enhancing bond
strength. Titanium also yields im-
use Continum C.
Continum C's coefficient of
thermal expansion is optimized for
proved anti-greening properties for
major porcelain brands such as
more esthetic restorations.
Ceramco, Noritake as well as other
commercial medium-grain porcelains.
When only the best will do…
ous casting technology yields an
Aalba Dent's proprietary continu-
Degassing Continum is not required,
saving technicians valuable time.
Continum C's titanium (Ti) acts as an
Tensile
Strength
Yield
Strength
Modulus of
Elasticity
Elongation
Percent
Vickers
Hardness
Density
Color
Coefficient of
Expansion
Melting Range
Composition
158,200
(1,091)
99,350
(685)
29.0 (0.20)
19
323
8.0
White
14.3
2,132-2,521
(1,167-1,383)
Ni 76.9%
Cr 15.0%
Mo 4.7%
Al, Be, Ti
psi (MPa)
Continum C
psi (MPa)
psi (MPa) X106
%
HV1
g/cm
3
(@500°C) X10-6
°F (°C)
17