Issue link: https://aalbadent.uberflip.com/i/107865
VeraBond V PFM:Ni-Cr-Mo ® V IS FOR VITA1 VeraBond V is a premium, high lain bond and increased porcelain-to- strength, nickel-chromium alloy with a metal retention. VeraBond V exhibits coefficient of thermal expansion exceptional oxidation control for a engineered to match Vita1 and other light, resilient oxide. With VeraBond V, European-type fine grain porcelains. you won't see dark finish lines at Its unique formulation provides your margins. superior properties; excellent porce- Processing VeraBond V is simple and trouble-free. VeraBond V possesses the minimum requirements required biocompatibility, and overall efficacy. superior melting and casting fluidity for in ISO 22674. You can create frame- With over three decades of clinical VeraBond V 204 gram box (40 ingots) your most intricate patterns. VeraBond works and crowns with greater service, VeraBond V has been proven to V's exceptional mechanical properties strength and less bulk. offer patients durability, comfort and Vera Solder 2 dwt (3.11 g) packet 2 gram packet permit the design of thin wall copings safety. Prescribe VeraBond V with and slender interproximal connections. vitro evaluations confirm and validate VeraBond V provides you with type 5 VeraBond V's corrosion resistance, Packaging & Accessories Vera Flux 1.5 oz jar (42.5 g) Numerous clinical studies and in 12 1 Vita mechanical properties which exceed Tensile Strength APPLICATIONS Porcelain fused to metal (PFM), single units, long-span bridgework, maryland bridge, metal sub-structure for polymer resins (acrylic & composites), full cast crowns, implant superstructures. confidence. PORCELAIN COMPATIBILITY VeraBond V performs best with traditional fine-grain porcelains: Vita, Ivoclar-Classic, Shofu-Vintage, Duceram, Will-Ceram, Finesse, as well as other commercially available fine-grain porcelains. Yield Strength 120,000 (828) 83,500 (576) psi (MPa) Verabond V psi (MPa) Elongation Percent % 10 Vickers Hardness HV1 380 Density Color 8.1 White g/cm3 Coefficient of Expansion (@500°C) X10-6 13.8 Melting Range Composition 2,124-2,282 (1,162-1,250) mark of Vita Zahnfabrik Ni 74.8% Cr 12.7% Mo 9.0% Al, Be, Co °F (°C) 13