PFM:Ni-Cr-Mo
alloys, unparalleled homogeneity, and precise alloy chemistry. Technicians will find more perfect castings, lighter oxides and improved bond strength. With its small, efficient ingot design (4.90g), Comandium melts fast, minimizing gas and oxide formation. Comandium's 14.3 CTE is optimized for major porcelain brands such as Ceramco, Noritake, as well as other medium-grain porcelains. Degassing Comandium is not required, saving technicians valuable time.
Comandium's titanium (Ti) acts as an oxygen scavenger, enhancing bond strength and chemically bonding
with the feldspar (SiO2) and kaolin (K2O), common to all porcelains. Titanium also improves anti-greening effects for more esthetic restorations.
For further economy,
Comandium is also available in a non-branded 200 gram package. Don't compromise, use Comandium.
Strength psi (MPa)
Tensile Comandium C
189,000 (1,303)
Strength psi (MPa)
Yield
127,600 (880)
Modulus of
Elasticity psi (MPa) X106
29.0 (0.20)
Elongation
Percent %
11
Hardness HV1
Vickers 352
Density g/cm3
8.0
Color White
Coefficient of
Expansion (@500°C) X10-6
14.3
Melting Range °F (°C)
2,129-2,363 (1,165-1,295)
Composition
Ni 78.0% Cr 13.0% Mo 4.7% Al, Be, Ti
21