PFM:Ni-Cr-Nb
Niobium provides excellent melting and casting fluidity for sharp margins and consistent castings every time. Second, a tightly controlled addition of 9% molybdenum creates high strength to offer uncommonly high resistance to
thermal or clinical distortion. High yield strength and great elongation make VeraBond 2V a winner. VeraBond 2V mechanical properties exceed industry standards by a factor of three! Low specific gravity, excellent castability and high yield strength permit the design of light weight, thin wall copings and fine interproximal abut- ments. Aesthetically pleasing and
comfortable restorations are now achievable like never before. VeraBond 2V… a clinically proven restoration you
can prescribe with confidence. 1Vita mark of Vita Zahnfabrik
Strength psi (MPa)
Tensile Verabond 2V
148,000 (1,021)
Strength psi (MPa)
Yield
108,000 (754)
Elongation
Percent %
18
Hardness HV1
Vickers 373
Density g/cm3
8.2
Color White
Coefficient of
Expansion (@500°C) X10-6
13.7
Melting Range °F (°C)
2,354-2,435 (1,290-1,335)
Composition
Ni 78.5% Cr 12.8% Mo 9.0% Nb, Al, Si
15
NIOM certified